材质，工艺求助

SANHAI

各位老师：今收到客户一样块，分光仪化验后材质成分如下：C  1.63%  Si  5.06% Mn  0.6%  S  0.0037%  P 0.0086% Cr  1.61% Ni  37.34%  Mo  0.98%  Fe  50.8%   
          Cu  0.094%  Al  0.012%.                这对应国内是哪种材料。铸造采用哪种工艺呢？这种材料有何特点？

yynnkk

这是做什么用的材质啊！C那么低，硅那么高！

wangyoufa

看成分感觉是耐热铁的化学成分，C的分析不知是否准确。

qls

6.1        Chemical Composition

: g7 K- y4 S2 |+ F. Y: CThe chemical composition of castings made to this specification shall conform to the requirements in the following table:
8 e9 a( @8 i5 ?) Z; c
Element        Weight %
        Minimum        Maximum
Carbon        -                  2.0
$ ~# p# V2 |7 b" r. FSilicon                  4.8                  5.3
Nickel                34.0                38.0
& p! E" J5 h1 w. \! K0 D2 {/ b3 u( bChromium                  1.6                  2.2
# j* C5 ~% s5 |; V* Q( N. v& eManganese        -                  0.7
Magnesium                  0.035                  0.09
Phosphorus        -                  0.07
Sulphur        -                  0.03
Rare Earth (total)        -                  0.01
( j; l7 O/ W% G* Others (each element)        -                  0.2
* Others (total)        -                  2.0
Iron        Balance
' R& I; f6 S3 ]
* See section 6.2.1
你看和这个材料要求是否相近。

nthdnhb1979

不用找了，如果猜了不错的话，应该是高镍奥氏体球墨铸铁，从事此类产品的生产时，如果仅仅局限于以凑得数的方式来熔炼的话---即仅保证成分合格不关心熔炼手法和过程的话，结果往往是全军覆没。我们以前有过几十万付之东流的惨痛教训。目前国内新伟贤，无锡某厂、圣得曼的金永锡等做了不错。上次看咱们论坛里也有几个同行攻克此难题。等待高人指点吧。

chp01861

如４楼所说的，是高镍奥氏体球墨铸铁,牌号为GGGNiSiCr35.52

xuwu531

高镍奥氏体球铁，石墨形态较难控制

xyzhlan

7# xuwu531
我想气孔也是件头痛的事情，这种材质确实不好搞

kyboZ

球墨铸铁的碳那么低？？？

nthdnhb1979

看看这篇帖子吧。这位同行做出来了。挺令咱们羡慕的。难度自然不必多讲了。做过的人都知道其中滋味。
/ p) B/ A! Q$ `8 n( J1 chttp://bbs.chinarjg.com/viewthre ... #pid121110pid121110

HCHLBHS

看过楼上推荐的贴子，感觉自己真是井底之蛙，佩服各位高人，以后得多努力啊。

无止境

为什么成分之中无稀土和美